- 吸水率 [%]: 0.14
- 缺口冲击强度: 6.4
- 拉伸强度 [MPa]: 41.0
- 断裂伸长率 [%]: 68.0
- 弯曲模量 [MPa]: 2.24
- 硬度: 115.0
- 热变形温度 [℃]: 129.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 | ||
| Water Absorption | 0.14 % @Time 86400 sec | 0.14 % @Time 24.0 hour | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 0.750 - 2.30 mm | 0.0080 - 0.011 in/in @Thickness 0.0295 - 0.0906 in | SABIC Method | ||
| 0.010 - 0.014 cm/cm @Thickness 2.30 - 4.60 mm | 0.010 - 0.014 in/in @Thickness 0.0906 - 0.181 in | SABIC Method | |||
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm @Thickness 0.750 - 2.30 mm | 0.0090 - 0.013 in/in @Thickness 0.0295 - 0.0906 in | SABIC Method | ||
| 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm | 0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in | SABIC Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 115 | 115 | ASTM D785 | ||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 | ||
| Flexural Strength | 68.0 MPa | 9860 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 | ||
| 1.70 J/cm @Temperature -40.0 °C | 3.18 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |||
| 1.92 J/cm @Temperature -30.0 °C | 3.60 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Gardner Impact | 37.0 J | 27.3 ft-lb | ASTM D3029 | ||
| 37.0 J | 27.3 ft-lb | ASTM D3029 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.7 @Frequency 1.00e+6 Hz | 5.7 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 8.5 @Frequency 100 Hz | 8.5 @Frequency 100 Hz | ASTM D150 | |||
| Dielectric Strength | 12.0 kV/mm @Thickness 3.20 mm | 305 kV/in @Thickness 0.126 in | in oil; ASTM D149 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | ASTM D150 | ||
| 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 | ||
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A | ||
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 79.2 µm/m-°C @Temperature -40.0 - 95.0 °C | 44.0 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 | |||
| 82.8 µm/m-°C @Temperature 60.0 - 138 °C | 46.0 µin/in-°F @Temperature 140 - 280 °F | ASTM E 831 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C @Thickness 6.40 mm | 264 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm | 250 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.760 mm | V-0 @Thickness 0.0299 in | UL 94 | ||
| 5VA @Thickness 2.20 mm | 5VA @Thickness 0.0866 in | UL 94 | |||
| Oxygen Index | 28.8 % | 28.8 % | ASTM D2863 | ||
| Descriptive Properties | |||||
| Specific Volume | 0.75cm^3/g | ASTM D792 | |||
| UV-light, water exposure/immersion | F2 | UL 746C | |||