- 熔体流动速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 1.2
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 84.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 100.0
- 透光率 [%]: 0.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Viscosity | 90000 cP | 90000 cP | Melt Viscosity, 300°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0050 in/in @Thickness 0.126 in | SABIC Method | |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C | 21 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| 37 g/10 min @Load 1.20 kg, Temperature 300 °C | 37 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
| Melt Index of Compound | 18 g/10 min @Load 2.16 kg, Temperature 265 °C | 18 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| 33 g/10 min @Load 1.20 kg, Temperature 300 °C | 33 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| 125 % | 125 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | 50 mm/min; ASTM D638 |
| 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| 0.200 J/cm @Temperature -30.0 °C | 0.375 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 0.950 J/cm @Temperature 0.000 °C | 1.78 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ASTM D4812 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature 0.000 °C | 2.86 ft-lb/in² @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | ISO 179/2C |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/2C | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/2C |
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179/2C | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 31.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 35.6 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 100 °C @Thickness 3.20 mm | 212 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 90.0 °C @Thickness 3.20 mm | 194 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 108 °C | 226 °F | Rate B/50; ASTM D1525 |
| 108 °C | 226 °F | Rate B/50; ISO 306 | |
| 110 °C | 230 °F | Rate B/120; ISO 306 | |
| 115 °C | 239 °F | Rate A/50; ISO 306 | |
| 115 °C | 239 °F | Rate A/50; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Haze | 89 % @Thickness 2.54 mm | 89 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 0.90 % | 0.90 % | 2.54 mm; ASTM D1003 |