- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.7
- 断裂伸长率 [%]: 118
- 弯曲强度 [MPa]: 74.0
- 弯曲模量 [MPa]: 8.70
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Flexural Modulus | 8.70 GPa | 1260 ksi | ASTM D790 |
| Compressive Yield Strength | 88.0 MPa | 12800 psi | ASTM D695 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 40 | 40 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
| Comparative Tracking Index | 265 V | 265 V | IEC test |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL-746B |
| Flammability, UL94 | HB @Thickness 1.59 mm | HB @Thickness 0.0625 in | |