- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.45
- 弯曲模量 [MPa]: 3.00
- 热变形温度 [℃]: 165.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.00 mm | 0.0020 in/in @Thickness 0.118 in | MD |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm @Thickness 3.00 mm | 0.0020 in/in @Thickness 0.118 in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | IEC Pub1.112, class 2; IEC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 205 °C | 401 °F | Ball pressure temperature; ASTM UL746B |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 265 °C | 509 °F | Molding temperature |
| Mold Temperature | 50.0 °C | 122 °F | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 3 hour | 3 hour | |