- 缺口冲击强度: 9.11
- 弯曲模量 [MPa]: 8.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | Laminate; ASTM D792 | ||
| 1.60 g/cc | 1.60 g/cc | Molded; ASTM D792 | |||
| Filler Content | 35 % | 35 % | By weight (ashing); Internal | ||
| Thickness | 3350 microns | 132 mil | Sheet; Internal | ||
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | Measured on flat plaques; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 | ||
| Tensile Modulus | 7.67 GPa | 1110 ksi | ISO 527 | ||
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 | ||
| Flexural Modulus | 8.22 GPa | 1190 ksi | ISO 178 | ||
| Poissons Ratio | 0.32 | 0.32 | ISO 527 | ||
| Izod Impact, Notched | 9.11 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 17.1 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | ||
| Impact Test | 26.9 J @Thickness 4.00 mm | 19.8 ft-lb @Thickness 0.157 in | Multi-axial, at failure; ASTM D3763 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 36.0 µm/m-°C @Temperature -40.0 - 120 °C | 20.0 µin/in-°F @Temperature -40.0 - 248 °F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Color | Black | Internal | |||