- 密度 [g/cm3]: 1.63
- 缺口冲击强度: 0.9
- 弯曲强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 9.60
- 热变形温度 [℃]: 276.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D 792 | ||
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 114 MPa | 16500 psi | ISO 527 | ||
| Tensile Strength, Ultimate | 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | ASTM D 638 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 | ||
| 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ASTM D 638 | |||
| Tensile Modulus | 10.8 GPa @Temperature 23.0 °C | 1570 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 | ||
| 180 MPa | 26100 psi | ASTM D 790 | |||
| Flexural Modulus | 9.60 GPa | 1390 ksi | ASTM D 790 | ||
| 10.0 GPa | 1450 ksi | ISO 178 | |||
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | ||
| Izod Impact, Unnotched | 6.90 J/cm @Temperature 23.0 °C | 12.9 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D 257 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 | ||
| Dielectric Constant | 3.0 @Frequency 10000 Hz, Temperature 23.0 °C | 3.0 @Frequency 10000 Hz, Temperature 73.4 °F | ASTM D 150 | ||
| 3.0 @Frequency 100000 Hz, Temperature 23.0 °C | 3.0 @Frequency 100000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.1 @Frequency 1000 Hz, Temperature 23.0 °C | 3.1 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| Dielectric Strength | 20.4 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 518 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s, Short Time; ASTM D149 | ||
| Dissipation Factor | 0.0020 @Frequency 100000 Hz | 0.0020 @Frequency 100000 Hz | ASTM D 150 | ||
| 0.0090 @Frequency 1.00e+6 Hz | 0.0090 @Frequency 1.00e+6 Hz | ASTM D 150 | |||
| 0.011 @Frequency 10000 Hz | 0.011 @Frequency 10000 Hz | ASTM D 150 | |||
| 0.014 @Frequency 1000 Hz | 0.014 @Frequency 1000 Hz | ASTM D 150 | |||
| Comparative Tracking Index | 440 V | 440 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 276 °C | 529 °F | ASTM D 648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| 255 °C | 491 °F | ASTM D 648 | |||
| UL RTI, Electrical | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | UL 746B | ||
| 150 °C @Thickness 3.00 mm | 302 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | UL 746B | ||
| 150 °C @Thickness 3.00 mm | 302 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 0.790 mm | V-2 @Thickness 0.0311 in | IEC 60695-11-10 | ||
| V-2 @Thickness 0.790 mm | V-2 @Thickness 0.0311 in | UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Features | Electrical Properties, Good | ||||
| Flame Retardant | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-GF30FR(17)< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Glass Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-GF30FR(17) | ISO 1043 | |||
| Uses | Connectors | ||||
| E/E Applications | |||||