- 密度 [g/cm3]: 1.58
- 缺口冲击强度: 0.45
- 弯曲强度 [MPa]: 99.0
- 弯曲模量 [MPa]: 6.75
- 热变形温度 [℃]: 272.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D 792 | ||
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Filler Content | 20 % | 20 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 84 | 84 | ASTM D 785 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Tensile Strength, Ultimate | 99.0 MPa @Temperature 23.0 °C | 14400 psi @Temperature 73.4 °F | ASTM D 638 | ||
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 | ||
| 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | ASTM D 638 | |||
| Tensile Modulus | 8.00 GPa @Temperature 23.0 °C | 1160 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 140 MPa | 20300 psi | ASTM D 790 | ||
| 145 MPa | 21000 psi | ISO 178 | |||
| Flexural Modulus | 6.75 GPa | 979 ksi | ASTM D 790 | ||
| 7.40 GPa | 1070 ksi | ISO 178 | |||
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C | 0.843 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | ||
| Izod Impact, Unnotched | 430 J/cm @Temperature 23.0 °C | 806 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D 257 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 | ||
| Dielectric Constant | 3.0 @Frequency 1000 Hz, Temperature 23.0 °C | 3.0 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D 150 | ||
| 3.0 @Frequency 10000 Hz, Temperature 23.0 °C | 3.0 @Frequency 10000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.0 @Frequency 100000 Hz, Temperature 23.0 °C | 3.0 @Frequency 100000 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| 3.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D 150 | |||
| Dielectric Strength | 20.7 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 526 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s, Short Time; ASTM D149 | ||
| Dissipation Factor | 0.0030 @Frequency 100000 Hz | 0.0030 @Frequency 100000 Hz | ASTM D 150 | ||
| 0.0080 @Frequency 1.00e+6 Hz | 0.0080 @Frequency 1.00e+6 Hz | ASTM D 150 | |||
| 0.013 @Frequency 1000 Hz | 0.013 @Frequency 1000 Hz | ASTM D 150 | |||
| 0.021 @Frequency 10000 Hz | 0.021 @Frequency 10000 Hz | ASTM D 150 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 272 °C | 522 °F | ASTM D 648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 | ||
| 234 °C | 453 °F | ASTM D 648 | |||
| UL RTI, Electrical | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | UL 746B | ||
| 150 °C @Thickness 3.00 mm | 302 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | ||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 100 °C | 212 °F | Optimum | ||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 95.0 °C | 203 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Features | Electrical Properties, Good | ||||
| Flame Retardant | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PCT | ||||
| Part Marking Code | >PCT-GF20FR(17)< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PCT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Glass Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-GF20FR(17) | ISO 1043 | |||
| Uses | Connectors | ||||
| E/E Applications | |||||