- 熔体流动速率 [g/10min]: 4.8
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM-D792 | ||
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 1320 % | 1320 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 1400 % | 1400 % | ASTM-D882 | ||
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 0.530 g/micron | 13.5 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 0.790 g/micron | 20.1 g/mil | ASTM-D1922 | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| 1% Secant Modulus, MD | 420 MPa | 60900 psi | ASTM-D882 | ||
| 1% Secant Modulus, TD | 430 MPa | 62400 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 88 % | 88 % | ASTM-D1003 | ||
| Gloss | 9.0 % | 9.0 % | Angle 60°; ASTM-D2457 | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 230-250 | Cast Films | |||
| Screen Package | 40/40 | mesh, 100% pure | |||
| 40/60/40 | mesh, Blend | ||||
| Temperature Profile (°C) | 190-230 | Cast Films | |||