- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238E | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 440 % | 440 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 15.7 g/micron | 400 g/mil | Notched; ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 31.5 g/micron | 800 g/mil | Notched; ASTM D1992 | ||
| Dart Drop | 4.09 g/micron | 104 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 29.6 MPa | 4300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 241 MPa | 35000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 18 % | 18 % | ASTM D1003 | ||
| Gloss | 50 % | 50 % | 45°; ASTM D2457 | ||
| 80 % | 80 % | 60°; ASTM D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 204 °C | 399 °F | |||
| Die Opening | 0.0762 cm | 0.0300 in | |||
| Extruder Size | 6.35 cm | 2.50 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||