- 熔体流动速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 10.3
- 弯曲强度 [MPa]: 12.4
- 弯曲模量 [MPa]: 0.310
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | |
| Melt Flow | 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.4 MPa | 1800 psi | ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D638 |
| Elongation at Break | 725 % | 725 % | ASTM D638 |
| Flexural Modulus | 0.310 GPa | 45.0 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+17 ohm-cm | 5.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.27 | 2.27 | ASTM 1531 |
| Dissipation Factor | 0.00010 | 0.00010 | ASTM 1531 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 °C | 401 °F | |