- 熔体流动速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 7.50 g/m²/day | 0.483 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.7 MPa | 1550 psi | ASTM D882 |
| Film Elongation at Break, MD | 640 % | 640 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Film Elongation at Yield, MD | 20 % | 20 % | ASTM D882 |
| Film Elongation at Yield, TD | 9.0 % | 9.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 320 g | 320 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 690 g | 690 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 25.1 MPa | 3640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.7 MPa | 3440 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |