- 熔体流动速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.34 MPa | 1210 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.31 MPa | 1060 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 | ||
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 | ||
| Puncture Energy | 4.41 J | 3.25 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength, MD | 7.382 g/micron | 187.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 22.6 g/micron | 575 g/mil | ASTM D1922 | ||
| Dart Drop | 6.89 g/micron | 175 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 66.9 MPa | 9700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 48.1 MPa | 6970 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 101 MPa | 14700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 114 °C | 237 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.2 % | 2.2 % | ASTM D1003 | ||
| Gloss | 87 % | 87 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||