- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.10 MPa | 1320 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 630 % | 630 % | ASTM D882 | ||
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 | ||
| Puncture Energy | 3.62 J | 2.67 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 18.1 g/micron | 460 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 23.6 g/micron | 600 g/mil | ASTM D1922 | ||
| Dart Drop | 13.0 g/micron | 330 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 62.6 MPa | 9080 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 50.8 MPa | 7370 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 163 MPa | 23700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 183 MPa | 26500 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 109 °C | 228 °F | ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 17 % | 17 % | ASTM D1003 | ||
| Gloss | 37 % | 37 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||