- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.939
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.758
- 热变形温度 [℃]: 54.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 400 hour | >= 400 hour | (10% Igepal), F50; ASTM D1693 |
| >= 1000 hour | >= 1000 hour | (100% Igepal), F50; ASTM D1693 | |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | 2" (50mm) per min.; ASTM D638 |
| Elongation at Yield | 11.3 % | 11.3 % | 2" (50mm) per min.; ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | 1.3mm per min; ASTM D790 |
| Dynatup @ -30°C | 81.3 J @Thickness 3.17 mm | 60.0 ft-lb @Thickness 0.125 in | ARM Std. Low Temp Impact; ARM Std. |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |