- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.91
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505-98 |
| Melt Flow | 1.6 - 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.6 - 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.80 MPa | 1420 psi | ASTM D882-02 |
| Film Tensile Strength at Yield, TD | 9.60 MPa | 1390 psi | ASTM D882-02 |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882-02 |
| Film Elongation at Break, TD | 870 % | 870 % | ASTM D882-02 |
| Film Elongation at Yield, MD | 43 % | 43 % | ASTM D882-02 |
| Film Elongation at Yield, TD | 36 % | 36 % | ASTM D882-02 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894-99 |
| Dart drop Test | 250 g | 0.551 lb | ASTM D1709-98 |
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | ASTM D882-02 |
| Film Tensile Strength at Break, TD | 47.0 MPa | 6820 psi | ASTM D882-02 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.2 % | 2.2 % | ASTM D1003A-00 |
| Gloss | 81 % | 81 % | ASTM D785-03 |