- 熔体流动速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 10.2
- 弯曲模量 [MPa]: 0.335
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D 792 |
| Melt Flow | 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D 2240 |
| Tensile Strength, Yield | 10.2 MPa | 1480 psi | ASTM D 638 |
| Elongation at Break | 600 % | 600 % | ASTM D 638 |
| Flexural Modulus | 0.335 GPa | 48.6 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D 1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D 746 |