- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 |
| Elmendorf Tear Strength MD | 135 g | 135 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.50 g/micron | 114 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.33 g/micron | 338.6 g/mil | ASTM D1922 |
| Dart drop Total Energy | 600 J/cm | 1.12 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 3.67 g/micron | 93.2 g/mil | ASTM D1709 |
| Dart drop Test | 110 g | 0.243 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 240 MPa | 34800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 80 % | 80 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 300 °C | 482 - 572 °F | |
| Roll Temperature | 20.0 °C | 68.0 °F | |