- 熔体流动速率 [g/10min]: 2.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.919 g/cc | 0.919 g/cc | ISO 1183 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 527-3 |
| Film Elongation at Break, MD | 850 % | 850 % | ISO 527-3 |
| Film Elongation at Break, TD | 900 % | 900 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 5.60 g/micron | 142 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 10.7 g/micron | 272 g/mil | ISO 6383-2 |
| Dart drop Test | 130 g | 0.287 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 215 MPa | 31200 psi | ISO 178 |
| 1% Secant Modulus, TD | 245 MPa | 35500 psi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | ISO 11357 |
| Vicat Softening Point | 100 °C | 212 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ISO 14782 |
| Gloss | 55 % | 55 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | Extrusion Temp |
| Die Opening | >= 0.180 cm | >= 0.0709 in | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | |