- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | AT Plastics PTM-03 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 400 % | 400 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.210 GPa | 30.5 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.240 GPa | 34.8 ksi | 1% Secant Modulus; ASTM D882 |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | Method A (500 mm/min); ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 54 % | 54 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 230 °C | 338 - 446 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |