- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 14.3
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | Base Resin; ASTM D1928/D 1505 |
| Degree of Crosslinking | 12 % | 12 % | ASTM D2765 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Yield | >= 14.3 MPa | >= 2070 psi | Heat Aging (168 hrs at 136°C); ASTM D638 |
| 15.9 MPa | 2300 psi | At 20 in/min; ASTM D638 | |
| Elongation at Break | <= 75 % | <= 75 % | Hot Creep Test (150°C,29 psi); ICEA T-28-562 |
| 360 % | 360 % | Heat Aging (168 hrs at 136°C); ASTM D412 | |
| 400 % | 400 % | ASTM D638 | |
| Tensile Set | 5.0 % | 5.0 % | Hot Creep Test (150°C,29 psi); ICEA-T-28-562 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | <= 2.3 @Frequency 50 Hz | <= 2.3 @Frequency 50 Hz | ASTM D150 |
| Dielectric Strength | >= 21.7 kV/mm | >= 550 kV/in | ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 50 Hz | 0.00050 @Frequency 50 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |