- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 1.0 hour @Thickness 3.00 mm, Temperature 23.0 °C | 1.0 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C | 22 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Hardness, Shore D | 49 | 49 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 483 % | 483 % | ASTM D638 |
| Secant Modulus | 0.209 GPa | 30.3 ksi | 0.01; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 7.8 % | 7.8 % | 60° angle; ASTM D2457 |