- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183-A |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 1184 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 1184 |
| Elmendorf Tear Strength MD | 500 g | 500 g | ISO 6283-2 |
| Elmendorf Tear Strength TD | 350 g | 350 g | ISO 6283-2 |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | ISO 6283-2 |
| Elmendorf Tear Strength, TD | 7.00 g/micron | 178 g/mil | ISO 6283-2 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F50; ISO 7765-A |
| Dart drop Test | 150 g | 0.331 lb | F50; ISO 7765-A |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ISO 1184 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 °C | 338 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |