- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 - 0.924 g/cc | 0.0333 - 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 1.7 - 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.7 - 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Tensile Strength at Break | 12.5 MPa | 1810 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 365 % | 365 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Secant Modulus, MD | 0.0950 GPa | 13.8 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.100 GPa | 14.5 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.65 | 0.65 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 8.40 g/micron | 213 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.60 g/micron | 142 g/mil | ASTM D1922 |
| Dart drop Test | 140 g | 0.309 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 109 % | 109 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 155 - 170 °C | 311 - 338 °F | Plasticizing Zone |
| 165 - 175 °C | 329 - 347 °F | Mixture Zone | |
| Feed Temperature | 145 - 160 °C | 293 - 320 °F | |
| Adapter Temperature | 175 - 190 °C | 347 - 374 °F | |