- 密度 [g/cm3]: 0.8985
- 弯曲模量 [MPa]: 0.117
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.8985 g/cc | 0.03246 lb/in³ | ASTM D792 |
| Melt Index of Compound | 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 91 | 91 | 1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 |
| 93 | 93 | 5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240 | |
| Tensile Strength at Break | 11.4 MPa | 1650 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 900 % | 900 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.117 GPa | 17.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 119 °C | 246 °F | Dow Method (DSC) |
| Glass Transition Temp, Tg | -52.2 °C | -62.0 °F | Dow Method |