- 熔体流动速率 [g/10min]: 2.25
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 10.8
- 弯曲模量 [MPa]: 0.269
- 脆化温度 [℃]: -73.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D4883 |
| Melt Flow | 2.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500 mm/min; ASTM D638 |
| Tensile Strength, Yield | 10.8 MPa | 1570 psi | 500 mm/min; ASTM D638 |
| Elongation at Break | 380 % | 380 % | 500 mm/min; ASTM D638 |
| Flexural Modulus | 0.269 GPa | 39.0 ksi | 2% Secant, 12.7 mm/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Brittleness Temperature | <= -73.0 °C | <= -99.4 °F | ASTM D746 |