- 熔体流动速率 [g/10min]: 0.8
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ISO 1183 |
| Thickness | 30.0 - 150 microns | 1.18 - 5.91 mil | Recommended |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 527-3 |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | 0.11 | 0.11 | ISO 8295 |
| Elmendorf Tear Strength, MD | 4.5855 g/micron | 116.47 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 6.114 g/micron | 155.3 g/mil | ISO 6383-2 |
| Dart drop Test | 180 g | 0.397 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 °C | 237 °F | Internal method |
| Vicat Softening Point | 95.0 °C @Load 1.00 kg | 203 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.5 % | 7.5 % | ISO 14782 |
| Gloss | 65 % | 65 % | 45°; ASTM D2457 |