- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.228
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.050 cm/cm | 0.010 - 0.050 in/in | 0.125 in; ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Modulus | 0.228 GPa | 33.0 ksi | 2% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | Rate A, Loading 1 (10 N); ASTM D1525 |