- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D1501 | ||
| Vinyl Acetate Content | 4.5 % | 4.5 % | |||
| Thickness | 31.8 microns | 1.25 mil | 2:1 BUR; 25 mil die gap | ||
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 140 g | 140 g | ASTM D1922 | ||
| Dart drop Test | 150 g | 0.331 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 77 % | 77 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Antiblock | None | ||||
| Slip | None | ||||