- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.6 g/10 min | 1.6 g/10 min | ASTM D1238 |
| Antiblock Level | 1000 ppm | 1000 ppm | |
| Slip Level | 300 ppm | 300 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Dart Drop | 1.57 g/micron | 40.0 g/mil | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 331 MPa | 48000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 379 MPa | 55000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 60°; ASTM D523 |