- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.919
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | molding; ASTM D2240 |
| Tensile Strength at Break | 10.3 MPa | 1500 psi | molding; ASTM D638 |
| Film Elongation at Break, MD | 220 % | 220 % | ASTM D882 |
| Film Elongation at Break, TD | 520 % | 520 % | ASTM D882 |
| Elongation at Break | 600 % | 600 % | molding; ASTM D638 |
| Elmendorf Tear Strength MD | 390 g | 390 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM D1922 |
| Dart Drop | 4.72 g/micron | 120 g/mil | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.8 MPa | 3600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
| 1% Secant Modulus, MD | 179 MPa | 26000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 228 MPa | 33000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | molding; ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | molding; ASTM D746 |
| 0.500 °C | 32.9 °F | molding, notched; ASTM D746 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 177 °C | 350 °F | |
| Die Opening | 0.0635 cm | 0.0250 in | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |