- 熔体流动速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.176 GPa | 25.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.186 GPa | 27.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 210 g | 210 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.82 g/micron | 224 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.61 g/micron | 168 g/mil | ASTM D1922 |
| Dart Drop | 2.68 g/micron | 68.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 85.0 g | 0.187 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 19.0 MPa | 2760 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 6.4 % | 6.4 % | ASTM D1003 |
| Gloss | 71 % | 71 % | 45°, ASTM D-2457 |