- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 78.7 microns | 3.10 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.20 MPa | 1330 psi | ASTM D882 |
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Break, TD | 630 % | 630 % | ASTM D882 |
| Secant Modulus, MD | 0.216 GPa | 31.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.245 GPa | 35.5 ksi | ASTM D882 |
| Coefficient of Friction | 0.12 | 0.12 | ASTM D1894 |
| Elmendorf Tear Strength MD | 1070 g | 1070 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1220 g | 1220 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.6 g/micron | 345 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 15.5 g/micron | 394 g/mil | ASTM D1922 |
| Dart Drop | 18.7 g/micron | 474 g/mil | F50; ASTM D1709 |
| Dart drop Test | 1470 g | 3.24 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 54.0 MPa | 7830 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.0 MPa | 7690 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 118 °C | 244 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 13.6 % | 13.6 % | ASTM D1003 |
| Gloss | 59 % | 59 % | 45°, ASTM D-2457 |