- 熔体流动速率 [g/10min]: 25.0
- 拉伸强度 [MPa]: 64.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 190 °C | 25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 @Thickness 3.17 mm | 50 @Thickness 0.125 in | Durometer, Injection Molded; ASTM D2240 | ||
| Tensile Strength at Break | 56.5 MPa @Thickness 3.17 mm | 8200 psi @Thickness 0.125 in | Injection Molded; ASTM D638 | ||
| Tensile Strength, Yield | 64.8 MPa @Thickness 3.17 mm | 9400 psi @Thickness 0.125 in | Injection Molded; ASTM D638 | ||
| Elongation at Yield | 19 % @Thickness 3.17 mm | 19 % @Thickness 0.125 in | Injection Molded; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 86.1 °C | 187 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Forms | Pellets | ||||
| Processing Method | Injection Molding | ||||