- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.93
- 拉伸强度 [MPa]: 14.0
- 弯曲强度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 300 % | 300 % | ASTM D882 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Modulus of Elasticity | 0.442 GPa | 64.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.366 GPa | 53.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.414 GPa | 60.0 ksi | ASTM D882 |
| Dart Drop | 2.56 g/micron | 65.0 g/mil | ASTM D1709 |
| Dart drop Test | 65.0 g | 0.143 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 19.0 MPa | 2760 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 55 % | 55 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 171 - 182 °C | 340 - 360 °F | |