- 密度 [g/cm3]: 0.914
- 拉伸强度 [MPa]: 9.0
- 脆化温度 [℃]: -45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.914 g/cc | 0.0330 lb/in³ | ASTM D1505 | ||
| Particle Size | >= 150 µm | >= 150 µm | pan, 10% | ||
| <= 500 µm | <= 500 µm | sieve < 5% | |||
| Melt Index of Compound | 22 g/10 min @Load 2.16 kg, Temperature 190 °C | 22 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM D638 | ||
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 90 % | 90 % | 50 mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 100 °C | 212 °F | DSC; ASTM D3418 | ||
| 140 °C | 284 °F | fusing temperature | |||
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 | ||
| Brittleness Temperature | -45.0 °C | -49.0 °F | ASTM D638 | ||
| Descriptive Properties | |||||
| Max Dry Flow | max 31 sec/100g | ASTM | |||