- 熔体流动速率 [g/10min]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 |
| Water Vapor Transmission | 12.0 g/m²/day | 0.773 g/100 in²/day | |
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50; ASTM D1693 |
| Thickness | 30.0 - 120 microns | 1.18 - 4.72 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Tear Strength | 275 kN/m | 1570 pli | MD; ASTM D1922 |
| 275 kN/m | 1570 pli | TD; ASTM D1922 | |
| Dart drop Test | 220 g | 0.485 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.6 MPa | 3130 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.6 MPa | 2990 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | DSC |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 80 % | 80 % | 60°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 | |