- 熔体流动速率 [g/10min]: 0.01
- 密度 [g/cm3]: 0.935
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.25
- 拉伸强度 [MPa]: 15.2
- 断裂伸长率 [%]: 25.0
- 弯曲强度 [MPa]: 11.7
- 弯曲模量 [MPa]: 0.586
- 热变形温度 [℃]: 48.0
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 - 1.01 g/cc | 0.0338 - 0.0365 lb/in³ | Average value: 0.954 g/cc Grade Count:266 |
| Volatiles | 0.00000900 - 0.100 % | 0.00000900 - 0.100 % | Average value: 0.0500 % Grade Count:3 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | Average value: 0.590 g/cc Grade Count:14 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:6 |
| Moisture Absorption at Equilibrium | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0167 % Grade Count:6 |
| Environmental Stress Crack Resistance | 3.00 - 5000 hour | 3.00 - 5000 hour | Average value: 339 hour Grade Count:168 |
| 15.0 - 1000 hour @Temperature 50.0 - 60.0 °C | 15.0 - 1000 hour @Temperature 122 - 140 °F | Average value: 228 hour Grade Count:20 | |
| 13.0 - 530 hour @Temperature 50.0 - 50.0 °C | 13.0 - 530 hour @Temperature 122 - 122 °F | Average value: 228 hour Grade Count:15 | |
| 13.0 - 530 hour @Thickness 1.90 - 2.00 mm | 13.0 - 530 hour @Thickness 0.0748 - 0.0787 in | Average value: 228 hour Grade Count:15 | |
| Thermal Stress Crack Resistance | 250 hour | 250 hour | Average value: 250 hour Grade Count:4 |
| Linear Mold Shrinkage | 0.0150 - 0.0500 cm/cm | 0.0150 - 0.0500 in/in | Average value: 0.0219 cm/cm Grade Count:4 |
| Melt Flow | 0.0100 - 55.0 g/10 min | 0.0100 - 55.0 g/10 min | Average value: 5.90 g/10 min Grade Count:267 |
| Ash | 0.0300 - 0.0600 % | 0.0300 - 0.0600 % | Average value: 0.0467 % Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57.0 - 73.0 | 57.0 - 73.0 | Average value: 64.9 Grade Count:105 |
| Tensile Strength, Ultimate | 11.7 - 44.0 MPa | 1700 - 6380 psi | Average value: 29.8 MPa Grade Count:84 |
| Tensile Strength, Yield | 15.2 - 42.1 MPa | 2200 - 6100 psi | Average value: 27.4 MPa Grade Count:227 |
| Elongation at Break | 7.00 - 2000 % | 7.00 - 2000 % | Average value: 652 % Grade Count:193 |
| Elongation at Yield | 6.00 - 600 % | 6.00 - 600 % | Average value: 59.8 % Grade Count:58 |
| Modulus of Elasticity | 0.650 - 2.07 GPa | 94.3 - 300 ksi | Average value: 1.26 GPa Grade Count:23 |
| Flexural Yield Strength | 25.0 - 28.0 MPa | 3630 - 4060 psi | Average value: 26.8 MPa Grade Count:4 |
| Flexural Modulus | 0.586 - 2.62 GPa | 85.0 - 380 ksi | Average value: 1.23 GPa Grade Count:213 |
| Secant Modulus | 1.00 - 1.36 GPa | 145 - 197 ksi | Average value: 1.11 GPa Grade Count:8 |
| Izod Impact, Notched | 0.250 - 5340 J/cm | 0.468 - 10000 ft-lb/in | Average value: 3.48 J/cm Grade Count:74 |
| Charpy Impact, Notched | 0.400 J/cm² - NB | 1.90 ft-lb/in² - NB | Average value: 2.08 J/cm² Grade Count:18 |
| 2.00 - 5.50 J/cm² @Temperature -30.0 - -30.0 °C | 9.52 - 26.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.50 J/cm² Grade Count:5 | |
| Tensile Impact Strength | 50.0 - 4800 kJ/m² | 23.8 - 2280 ft-lb/in² | Average value: 276 kJ/m² Grade Count:65 |
| 100 - 200 kJ/m² @Temperature -30.0 - -30.0 °C | 47.6 - 95.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 149 kJ/m² Grade Count:4 | |
| Tensile Impact | 53.4 - 131 J/cm | 100 - 245 ft-lb/in | Average value: 79.7 J/cm Grade Count:17 |
| Tensile Creep Modulus, 1 hour | 360 - 510 MPa | 52200 - 74000 psi | Average value: 413 MPa Grade Count:6 |
| Tensile Creep Modulus, 1000 hours | 250 - 340 MPa | 36300 - 49300 psi | Average value: 282 MPa Grade Count:6 |
| Tear Strength Test | 23.5 - 30.0 | 23.5 - 30.0 | Average value: 28.4 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 1.00e+15 ohm-cm | 10000 - 1.00e+15 ohm-cm | Average value: 8.57e+14 ohm-cm Grade Count:7 |
| Surface Resistance | 10000 - 1.00e+14 ohm | 10000 - 1.00e+14 ohm | Average value: 8.57e+13 ohm Grade Count:7 |
| Dielectric Constant | 2.40 | 2.40 | Average value: 2.40 Grade Count:6 |
| Dielectric Strength | 150 kV/mm | 3810 kV/in | Average value: 150 kV/mm Grade Count:6 |
| Dissipation Factor | 0.000200 | 0.000200 | Average value: 0.000200 Grade Count:6 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 180 µm/m-°C | 10.0 - 100 µin/in-°F | Average value: 124 µm/m-°C Grade Count:18 |
| Melting Point | 124 - 135 °C | 255 - 275 °F | Average value: 130 °C Grade Count:33 |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 - 99.0 °C | 118 - 210 °F | Average value: 74.1 °C Grade Count:88 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 - 46.0 °C | 108 - 115 °F | Average value: 43.7 °C Grade Count:6 |
| Vicat Softening Point | 62.0 - 131 °C | 144 - 268 °F | Average value: 123 °C Grade Count:135 |
| Softening Point | 70.0 - 80.0 °C | 158 - 176 °F | Average value: 76.8 °C Grade Count:4 |
| Heat Distortion Temperature | 38.0 - 75.0 °C | 100 - 167 °F | Average value: 58.2 °C Grade Count:3 |
| Brittleness Temperature | -118 - 180 °C | -180 - 356 °F | Average value: -79.0 °C Grade Count:138 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:7 |
| Oxygen Index | 17.0 % | 17.0 % | Average value: 17.0 % Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Gloss | 25.0 - 90.0 % | 25.0 - 90.0 % | Average value: 41.7 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 240 °C | 340 - 464 °F | Average value: 196 °C Grade Count:22 |
| Die Temperature | 175 - 204 °C | 347 - 399 °F | Average value: 189 °C Grade Count:4 |
| Melt Temperature | 130 - 280 °C | 266 - 536 °F | Average value: 194 °C Grade Count:52 |
| Head Temperature | 185 - 204 °C | 365 - 399 °F | Average value: 194 °C Grade Count:3 |