- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.96
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.28
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 | ||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 65 | 65 | ASTM D2240 | ||
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.28 GPa | 185 ksi | Tangent Method 1; ASTM D-790 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||
| region | Europe/Turkey | ||||