- 拉伸强度 [MPa]: 29.3
- 热变形温度 [℃]: 77.0
- 脆化温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ASTM D792 |
| Melt Index of Compound | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength, Yield | 29.3 MPa | 4250 psi | 2"/min; ASTM D638 |
| Elongation at Break | 260 % | 260 % | 2"/min; ASTM D638 |
| Flexural Stiffness | 827 MPa | 120000 psi | ASTM D747 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | 75.0 °C | 167 °F | ASTM D746 |