- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 26.0
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | >= 300 hour | >= 300 hour | Antarox 10%; ASTM D1693-A |
| Melt Flow | 2.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 2.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ISO 868 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 3.00 J/cm² @Temperature -20.0 °C | 14.3 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA |
| 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |