- 熔体流动速率 [g/10min]: 0.29
- 密度 [g/cm3]: 0.954
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.378
- 热变形温度 [℃]: 68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 22 hour @Thickness 3.00 mm, Temperature 23.0 °C | 22 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693B |
| Melt Flow | 0.29 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.29 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 35 g/10 min @Load 21.6 kg, Temperature 190 °C | 35 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Flexural Modulus | 1.378 GPa | 199.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |