- 熔体流动速率 [g/10min]: 0.83
- 密度 [g/cm3]: 0.946
- 缺口冲击强度: 0.65
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 950
- 热变形温度 [℃]: 69.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | 139 hour @Thickness 2.00 mm, Temperature 50.0 °C | 139 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 0.83 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.83 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM-D2240 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM-D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM-D638 |
| Elongation at Break | 980 % | 980 % | ASTM-D638 |
| Elongation at Yield | 11 % | 11 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 950 MPa | 138000 psi | ASTM-D790 |
| Izod Impact, Notched | 0.650 J/cm | 1.22 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM-D648 |
| Vicat Softening Point | 121 °C @Load 1.02 kg | 250 °F @Load 2.25 lb | ASTM-D1525 |