- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.952
- 缺口冲击强度: 8.9
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 960
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM-D792 |
| ESCR 100% Igepal® | 200 hour @Thickness 2.00 mm, Temperature 50.0 °C | 200 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal® | 37 hour @Thickness 2.00 mm, Temperature 50.0 °C | 37 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 2.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 2.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM-D2240 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM-D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM-D638 |
| Flexural Modulus, 1% Secant | 960 MPa | 139000 psi | ASTM-D790 |
| Izod Impact, Notched | 8.90 J/cm | 16.7 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM-D648 |
| Vicat Softening Point | 129 °C @Load 1.02 kg | 264 °F @Load 2.25 lb | ASTM-D1525 |