- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1.07
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 90 hour | 90 hour | Condition B; ASTM D1693 |
| Melt Index of Compound | 6.0 g/10 min | 6.0 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 2 in/min, Type IV bar; ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | 2 in/min, Type IV bar; ASTM D638 |
| Flexural Modulus | 1.07 GPa | 155 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 121 °C | 250 °F | Loading 1, Rate A; ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, type 1 specimen; ASTM D746 |