- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.378
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 35 hour | 35 hour | Condition A, F50 CO-630 |
| 45 hour | 45 hour | Condition A, F50 CO-630; ASTM D1693 | |
| ESCR, Bottle | 250 hour @Temperature 60.0 °C | 250 hour @Temperature 140 °F | F50 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 2 in per min; ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 1.378 GPa | 199.9 ksi | 0.5"/min crosshead speed; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 182 °C | 340 - 360 °F | Thermoforming Surface |
| 171 - 204 °C | 340 - 399 °F | Blow Molding | |
| 194 - 216 °C | 381 - 421 °F | Extrusion | |