- 熔体流动速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 25.5
- 弯曲模量 [MPa]: 0.970
- 脆化温度 [℃]: -71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Melt Flow | 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 299 g/10 min @Load 21.6 kg, Temperature 190 °C | 299 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| Flexural Modulus | 0.970 GPa | 141 ksi | 3 pt. secant; ASTM D790 |
| 1.24 GPa | 180 ksi | 3 pt. Tangent; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -71.0 °C | <= -95.8 °F | ASTM D746 |