- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.38
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 35 hour | 35 hour | Cond. B; F50; ASTM D1693 |
| 45 hour | 45 hour | Cond. A; 100% Igepal® CO-630; F50; ASTM D1693 | |
| 250 hour @Temperature 60.0 °C | 250 hour @Temperature 140 °F | Bottle; F50; 10 ounce, 23-gram bottle, 10% fill, Joy Dishwashing liquid | |
| High Load Melt Index | 40 g/10 min @Load 21.6 kg, Temperature 190 °C | 40 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | Type IV; 50 mm per min; ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | Type IV; 50 mm per min; ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | 0.5"/min crosshead speed; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 182 °C | 340 - 360 °F | Thermoforming Surface Temp |
| 171 - 204 °C | 340 - 399 °F | Blow Molding Stock | |
| 194 - 216 °C | 381 - 421 °F | Extrusion Stock | |