- 熔体流动速率 [g/10min]: 0.26
- 密度 [g/cm3]: 0.951
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 0.26 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.26 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| High Load Melt Index | 30 g/10 min @Load 21.6 kg, Temperature 190 °C | 30 g/10 min @Load 47.6 lb, Temperature 374 °F | High Load Melt Index; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 0.750 GPa | 109 ksi | ASTM D882 |
| Secant Modulus, TD | 0.910 GPa | 132 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.394 g/micron | 10.0 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.33 g/micron | 110 g/mil | ASTM D1922 |
| Dart Drop | <= 1.20 g/micron | <= 30.5 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 °C | 430 °F | |