- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.962
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 43.0
- 弯曲模量 [MPa]: 1.814
- 热变形温度 [℃]: 73.0
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D4883 |
| Apparent Bulk Density | 0.590 g/cc | 0.0213 lb/in³ | ASTM D1895 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Modulus | 1.814 GPa | 263.1 ksi | 1% Secant; ASTM D 790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |