- 密度 [g/cm3]: 0.96
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 1.79
- 热变形温度 [℃]: 82.2
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50; ASTM D1693 |
| >= 500 hour | >= 500 hour | F50; ASTM D2561 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Flexural Strength | 35.0 MPa | 5070 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | -76.1 °C | -105 °F | ASTM D746 |